TAILIEUCHUNG - Electrocatalysis by nanoparticles: Oxidation of formic acid at manganese oxide nanorods-modified Pt planar and nanohole-arrays

The electro-oxidation of formic acid (an essential reaction in direct formic acid fuel cells) is a challenging process because of the deactivation of anodes by the adsorption of the poisoning intermediate carbon monoxide (CO). Pt electrodes in two geometries (planar and nanohole-array) were modified by the electrodeposition of manganese oxide nanorods (nano-MnOx). The modified Pt electrodes were then tested for their electrocatalytic activity through the electro-oxidation of formic acid in a solution of pH . Two oxidation peaks (I d p and I ind p ) were observed at and V, respectively; these were assigned to the direct and indirect oxidative pathways. A significant enhancement of the direct oxidation of formic acid to CO2 was observed at the modified electrodes, while the formation of the poisoning intermediate CO was suppressed. I d p increases with surface coverage (h) of nano-MnOx with a concurrent depression of I ind p . An increase in the ratio I d p/m 1/2 with decreasing potential scan rate (m) indicates that the oxidation process proceeds via a catalytic mechanism. The modification of Pt anodes with manganese oxide nanorods results in a significant improvement of the electrocatalytic activity along with a higher tolerance to CO. Thus nano-MnOx plays a crucial role as a catalytic mediator which facilitates the charge transfer during the direct oxidation of formic acid to CO2. | Electrocatalysis by nanoparticles: Oxidation of formic acid at manganese oxide nanorods-modified Pt planar and nanohole-arrays

• Hoá học
• Nanohole arrays
• Manganese oxide nanorods
• Modified surfaces
• Manganese oxide nanorods modified Pt planar
• Nanohole arrays