TAILIEUCHUNG - Magnetic and magnetotransport properties of La0.7Ca0.3Mn1-x(Zn,Cu)xO3

Magnetic and magnetotransport properties of two perovskite manganite samples of and prepared by conventional solid-state reaction have been studied in detail. Experimental results revealed that the temperature dependences of magnetization and resistance varied strongly around the phase-transition temperature. Maximum magnetoresistance (MR) values of and under an applied field of 400 Oe were about % and %, respectively. The maximum magnetic-entropy change (ΔSM) was J/ for , and J/ for when the applied field was 45 kOe. Both the MR and ΔSM values obtained from two samples were smaller than those of the parent compound . This was due to the change in the Mn3+/Mn4+ ratio caused by Zn and Cu dopants, which led to a change in the type of the ferromagneticparamagnetic phase transition. | Magnetic and magnetotransport properties of (Zn,Cu)xO3

Đã phát hiện trình chặn quảng cáo AdBlock
Trang web này phụ thuộc vào doanh thu từ số lần hiển thị quảng cáo để tồn tại. Vui lòng tắt trình chặn quảng cáo của bạn hoặc tạm dừng tính năng chặn quảng cáo cho trang web này.