TAILIEUCHUNG - Elucidating the chemical state of elements in CaO-CuO-CeO2 mixed oxide by X-ray photoelectron spectroscopy

In this research, three-component-oxide CaO-CuO-CeO2 was fabricated a sol-gel method. This mixed oxide acted as the catalysts for the complete oxidation of phenol in the presence of hydro peroxide. The activity of the catalyst was monitored versus fabrication conditions of mixed oxide such as aging temperature, calcination temperature and time. Under the optimum conditions including aging temperature at 70 oC, calcination at 600 oC for 30 min, the catalyst gave the best activity with phenol conversion. | Vietnam Journal of Chemistry, International Edition, 55(5): 645-651, 2017 DOI: Elucidating the chemical state of elements in CaO-CuO-CeO2 mixed oxide by X-ray photoelectron spectroscopy Pham Anh Son*, Hoang Thi Huong Hue Faculty of Chemistry, Hanoi University of Science, VNU Hanoi Received 14 April 2017; Accepted for publication 20 October 2017 Abstract In this research, three-component-oxide CaO-CuO-CeO2 was fabricated a sol-gel method. This mixed oxide acted as the catalysts for the complete oxidation of phenol in the presence of hydro peroxide. The activity of the catalyst was monitored versus fabrication conditions of mixed oxide such as aging temperature, calcination temperature and time. Under the optimum conditions including aging temperature at 70 oC, calcination at 600 oC for 30 min, the catalyst gave the best activity with phenol conversion. Among tested mixed oxides or single oxides, three-component-oxide CaO-CuO-CeO2 exhibited the highest performance. The chemical state of metal elements in the mixed oxide was carefully studied by high-resolution X-ray photoelectron spectroscopy (XPS) technique. The XPS spectra of Ca 2p, Cu 2p, and Ce 3d were recorded in ranges of 935-965, 927-967, and 878-930 eV, respectively. The curve fitting processes were carried out on CasaXPS version software with Shirley or Tougaard background and GL(m) line shape. Some constraints such as the FWHM, splitting energy and peak area ratio of spin-orbit interaction were introduced into the fitting process in order to achieve the highest physical meaning of the spectrum deconvolution. The fitting result proved the coexistence of Ce4+, Ce3+, Cu2+ and Cu+ in the component of the prepared material. The formation of Ce3+ and Cu+ from the interaction between Ce4+ and Cu2+ accompanied the appearance of oxygen vacancies in the crystal structure of CeO2 support. That process was enhanced by the presence of calcium element. Oxygen vacancies .

TỪ KHÓA LIÊN QUAN
TAILIEUCHUNG - Chia sẻ tài liệu không giới hạn
Địa chỉ : 444 Hoang Hoa Tham, Hanoi, Viet Nam
Website : tailieuchung.com
Email : tailieuchung20@gmail.com
Tailieuchung.com là thư viện tài liệu trực tuyến, nơi chia sẽ trao đổi hàng triệu tài liệu như luận văn đồ án, sách, giáo trình, đề thi.
Chúng tôi không chịu trách nhiệm liên quan đến các vấn đề bản quyền nội dung tài liệu được thành viên tự nguyện đăng tải lên, nếu phát hiện thấy tài liệu xấu hoặc tài liệu có bản quyền xin hãy email cho chúng tôi.
Đã phát hiện trình chặn quảng cáo AdBlock
Trang web này phụ thuộc vào doanh thu từ số lần hiển thị quảng cáo để tồn tại. Vui lòng tắt trình chặn quảng cáo của bạn hoặc tạm dừng tính năng chặn quảng cáo cho trang web này.