TAILIEUCHUNG - Preparation and spectroscopic properties of Ca2Al2SiO7: Tb3+ phosphor

The Tb3+ rare-earth-ion-doped Ca2Al2SiO7 material has a tetragonal phase structure that was successfully synthesized using the solid-state reaction method under optimal conditions: sintering temperature: 1280 °C; time: 60 minutes; and the B2O3 flux agent content: 4% wt. The photoluminescence spectrum of Tb3+ doped Ca2Al2SiO7 phosphor consists of narrow lines with peaks at 545, 440, 462, 494, 590, and 622 nm that correspond to 4f electronic transitions of the Tb3+ ion. The peak at 545 nm has the highest luminescent intensity. The influence of synthesis technology and the luminescent characteristics of the phosphor are presented and discussed. |

TAILIEUCHUNG - Chia sẻ tài liệu không giới hạn
Địa chỉ : 444 Hoang Hoa Tham, Hanoi, Viet Nam
Website : tailieuchung.com
Email : tailieuchung20@gmail.com
Tailieuchung.com là thư viện tài liệu trực tuyến, nơi chia sẽ trao đổi hàng triệu tài liệu như luận văn đồ án, sách, giáo trình, đề thi.
Chúng tôi không chịu trách nhiệm liên quan đến các vấn đề bản quyền nội dung tài liệu được thành viên tự nguyện đăng tải lên, nếu phát hiện thấy tài liệu xấu hoặc tài liệu có bản quyền xin hãy email cho chúng tôi.
Đã phát hiện trình chặn quảng cáo AdBlock
Trang web này phụ thuộc vào doanh thu từ số lần hiển thị quảng cáo để tồn tại. Vui lòng tắt trình chặn quảng cáo của bạn hoặc tạm dừng tính năng chặn quảng cáo cho trang web này.