TAILIEUCHUNG - Synthesis and application of graphene/silver nanowires/gold nanoparticles hybrid for ammonia gas sensing

With one-dimensional nanostructure, the AgNWs connects effectively together many rGO islands and reduce significantly their contact resistance so that NH3 sensing signal is improved and complete recovery of the sensor is nearly achieved at room temperature. Especially, all these signals are further enhanced when the AuNPs (diameter ~ 30 nm) are added into the hybrid. | Journal of Science and Technology 54 (1A) (2016) 175-182 SYNTHESIS AND APPLICATION OF GRAPHENE/SILVER NANOWIRES/GOLD NANOPARTICLES HYBRID FOR AMMONIA GAS SENSING Huynh Tran My Hoa*, Truong Thi Hoa, Truong Thu Hoai Huong, Nguyen Thi Yen Linh, Tran Quang Trung* Department of Solid State Physics, Faculty of Physics, University of Science, Vietnam National University, HCM City, 227 Nguyen Van Cu, Distr. 5, Ho Chi Minh City, Vietnam * Email: myhoa1910@; trungvlcr@ Received: 1 September 2015; Accepted for publication: 28 October 2015 ABSTRACT Graphene material synthesized from chemical method (reduced Graphene Oxide – rGO) is a promising candidate for gas sensors due to their unique properties. With structure of single layer of bonded sp2 carbons in a two-dimensional (2D) lattice, rGO have large surface to volume ratio, high conductivity and electron mobility at room temperature. Meanwhile, the different oxygencontaining functional groups (contain dangling bonds) decorated on carbon networks make rGO easily respond with compatible gas molecules. However, the investigating of structure of rGO in micrometer scale shows that the chemical method often results in non-uniform film thickness on substrate due to overlap of rGO sheets. These may disrupt the conductive paths in rGO films and decrease their conductivity. Therefore, gas sensing signal of pristine rGO based sensors is tarnished and the sensors do not recover to their baseline at room temperature. In this study, silver nanowires (AgNWs) and gold nanoparticles (AuNPs) are combined with rGO material to form rGO/AgNWs/AuNPs hybrid. With one-dimensional nanostructure, the AgNWs connects effectively together many rGO islands and reduce significantly their contact resistance so that NH3 sensing signal is improved and complete recovery of the sensor is nearly achieved at room temperature. Especially, all these signals are further enhanced when the AuNPs (diameter ~ 30 nm) are added into the .

TỪ KHÓA LIÊN QUAN
TAILIEUCHUNG - Chia sẻ tài liệu không giới hạn
Địa chỉ : 444 Hoang Hoa Tham, Hanoi, Viet Nam
Website : tailieuchung.com
Email : tailieuchung20@gmail.com
Tailieuchung.com là thư viện tài liệu trực tuyến, nơi chia sẽ trao đổi hàng triệu tài liệu như luận văn đồ án, sách, giáo trình, đề thi.
Chúng tôi không chịu trách nhiệm liên quan đến các vấn đề bản quyền nội dung tài liệu được thành viên tự nguyện đăng tải lên, nếu phát hiện thấy tài liệu xấu hoặc tài liệu có bản quyền xin hãy email cho chúng tôi.
Đã phát hiện trình chặn quảng cáo AdBlock
Trang web này phụ thuộc vào doanh thu từ số lần hiển thị quảng cáo để tồn tại. Vui lòng tắt trình chặn quảng cáo của bạn hoặc tạm dừng tính năng chặn quảng cáo cho trang web này.