TAILIEUCHUNG - A close correlation between disorders defects and superconducting transition temperature of Bi1.6Pb0.4Sr2Ca2-xNaxCu3O10+δ superconductors

The enhancements of zero superconducting transition temperature (Tc,0) in xNaxCu3O10+δ (BPSCCO) are reported. The BPSCCO samples (with x ranging from to ) were prepared by using the conventional solid state reaction technique. | Vietnam Journal of Science and Technology 56 (1A) (2018) 41-49 A CLOSE CORRELATION BETWEEN DISORDERS-DEFECTS AND SUPERCONDUCTING TRANSITION TEMPERATURE OF SUPERCONDUCTORS Tran Hai Duc1, *, Nguyen Khac Man2, Dang Thi Bich Hop3 1 Faculty of Physics, VNU University of Science, 334 Nguyen Trai, Ha Noi, Viet Nam 2 International Training Institute for Materials Science (ITIMS), Hanoi University of Science and Technology, 1 Dai Co Viet, Ha Noi, Viet Nam 3 Faculty of Basic Sciences, University of Transport Technology, 54 Trieu Khuc, Ha Noi, Viet Nam * Email: dhtran@ Received: 15 August 2017; Accepted for publication: 30 March 2018 ABSTRACT The enhancements of zero superconducting transition temperature (Tc,0) in (BPSCCO) are reported. The BPSCCO samples (with x ranging from to ) were prepared by using the conventional solid state reaction technique. The properties of the samples were examined by using the X-ray diffraction (XRD), scanning electron microscopy (SEM), and the resistance versus temperature (R-T) measurements. From the XRD resuts, all samples revealed the orthorhombic structure, and the volume fraction of the Bi-2223 phase was varied as increasing x, and reached the maximum value of % for x = sample. Improvements of connectivity between the Bi-2223 grains in the Na-substituted BPSCCO samples were obtained by using the surface SEM images and a quantitive analysis of a correlation between Tc,0 and residual resistance ratio (RRR). A similar variation of T c,0 of the samples as increasing x was observed. The highest Tc,0 enhancement of K was obtained for x = sample. Variations of the hole carrier concentrations in the CuO2 layers were investigated, which also showed the highest value achieved for x = sample. Keywords: BPSCCO, Bi-2223, Tc,0, RRR 1. INTRODUCTION In recent years, studies on applications of high temperature superconductors (HTS) have been .

TỪ KHÓA LIÊN QUAN
TAILIEUCHUNG - Chia sẻ tài liệu không giới hạn
Địa chỉ : 444 Hoang Hoa Tham, Hanoi, Viet Nam
Website : tailieuchung.com
Email : tailieuchung20@gmail.com
Tailieuchung.com là thư viện tài liệu trực tuyến, nơi chia sẽ trao đổi hàng triệu tài liệu như luận văn đồ án, sách, giáo trình, đề thi.
Chúng tôi không chịu trách nhiệm liên quan đến các vấn đề bản quyền nội dung tài liệu được thành viên tự nguyện đăng tải lên, nếu phát hiện thấy tài liệu xấu hoặc tài liệu có bản quyền xin hãy email cho chúng tôi.
Đã phát hiện trình chặn quảng cáo AdBlock
Trang web này phụ thuộc vào doanh thu từ số lần hiển thị quảng cáo để tồn tại. Vui lòng tắt trình chặn quảng cáo của bạn hoặc tạm dừng tính năng chặn quảng cáo cho trang web này.