TAILIEUCHUNG - Application of a dynamic-nanoindentation method to analyze the local structure of an Fe-18 at.% Gd cast alloy

A dynamic nanoindentation method was applied to study an Fe-18 at.% Gd alloy as a neutron-absorbing material prepared by vacuum arc-melting and cast in a mold. The Fe-18 at.% Gd cast alloy had a microstructure with matrix phases and an Fe-rich primary dendrite of Fe9Gd. Rietveld refinement of the X-ray spectra showed that the Fe-18 at.% Gd cast alloy consisted of at.% Fe3Gd, at.% Fe5Gd, at.% Fe9Gd, at.% Fe2Gd, and at.% b-Fe17Gd2. The average nanohardness of the primary dendrite phase and the matrix phases were GPa and GPa, respectively. | Application of a dynamic-nanoindentation method to analyze the local structure of an Fe-18 at.% Gd cast alloy N u c l e a r E n g i n e e r i n g a n d T e c h n o l o g y 4 9 ( 2 0 1 7 ) 5 7 6 e5 8 0 Available online at ScienceDirect Nuclear Engineering and Technology journal homepage: Original Article Application of a Dynamic-Nanoindentation Method to Analyze the Local Structure of an Fe-18 at.% Gd Cast Alloy Yong Choi a, Youl Baik a, Byung M. Moon b, and Dong-Seong Sohn c,* a Department of Materials Science and Technology, Dankook University, 119 Dandae-ro, Dongnam-gu, Cheonan, Chungnam 31116, South Korea b Liquid Processing and Casting Technology R and D Group, KITECH, 156 Gaetbeol-ro, Yeonsu-gu, Incheon, 21999, South Korea c Nuclear Engineering Department, UNIST, 50 UNIST-gil, Eonyang-eup, Ulju-gun, Ulsan, 689-798, South Korea article info abstract Article history: A dynamic nanoindentation method was applied to study an Fe-18 at.% Gd alloy as a Received 11 February 2016 neutron-absorbing material prepared by vacuum arc-melting and cast in a mold. The Fe-18 Received in revised form at.% Gd cast alloy had a microstructure with matrix phases and an Fe-rich primary 3 September 2016 dendrite of Fe9Gd. Rietveld refinement of the X-ray spectra showed that the Fe-18 at.% Gd Accepted 3 October 2016 cast alloy consisted of at.% Fe3Gd, at.% Fe5Gd, at.% Fe9Gd, at.% Fe2Gd, Available online 24 October 2016 and at.% b-Fe17Gd2. The average nanohardness of the primary dendrite phase and the matrix phases were GPa and GPa, respectively. The fatigue limit of the matrix phase Keywords: was approximately 37% higher than that of the primary dendrite phase. The dynamic Fe-Gd Cast Alloy nanoindentation method is useful for identifying local phases and for analyzing local Nano-indentation mechanical properties. Neutron-absorbing Materials Copyright © 2016, .

TỪ KHÓA LIÊN QUAN
TAILIEUCHUNG - Chia sẻ tài liệu không giới hạn
Địa chỉ : 444 Hoang Hoa Tham, Hanoi, Viet Nam
Website : tailieuchung.com
Email : tailieuchung20@gmail.com
Tailieuchung.com là thư viện tài liệu trực tuyến, nơi chia sẽ trao đổi hàng triệu tài liệu như luận văn đồ án, sách, giáo trình, đề thi.
Chúng tôi không chịu trách nhiệm liên quan đến các vấn đề bản quyền nội dung tài liệu được thành viên tự nguyện đăng tải lên, nếu phát hiện thấy tài liệu xấu hoặc tài liệu có bản quyền xin hãy email cho chúng tôi.
Đã phát hiện trình chặn quảng cáo AdBlock
Trang web này phụ thuộc vào doanh thu từ số lần hiển thị quảng cáo để tồn tại. Vui lòng tắt trình chặn quảng cáo của bạn hoặc tạm dừng tính năng chặn quảng cáo cho trang web này.