Fibrous properties of rayon has been modified through synthesis of graft copolymers of rayon with acrylonitrile (AN) by chemical method using ceric ammonium nitrate (CAN/HNO3) as a redox initiator and gamma radiation mutual method. Percentage of grafting (Pg) was determined as a function of initiator concentration, monomer concentration, irradiation dose, temperature, time of reaction and the amount of water. Maximum percentage of grafting (160.01%) using CAN/HNO3 was obtained at [CAN] = 22.80 • 103 mol/L, [HNO3] = 112.68 • 102 mol/L and [AN] = 114.49 • 102 mol/L in 20 mL of water at 45 C within 120 min while in case of gamma radiation method, maximum Pg (90.24%) was obtained at an optimum concentration of AN of 76.32 • 102 mol/L using 10 mL of water at room temperature with total dose exposure of 3.456 kGy/h. The grafted fiber was characterized by FTIR, SEM, TGA and XRD studies. Swelling behavior of grafted rayon in different solvents such as water, methanol, ethanol, DMF and acetone was studied and compared with the unmodified rayon. Dyeing behavior of the grafted fiber was also investigated. | Modification of fiber properties through grafting of acrylonitrile to rayon by chemical and radiation methods