The objective of this study was to determine the effect of mimosa bark usage on the formaldehyde emission, physical and mechanical properties of particleboard. Fifteen panels from black locust (Robinia pseudoacacia L.) wood containing mimosa bark in a core layer at different ratios were manufactured. | Turk J Agric For 29 (2005) 227-230 © TÜB‹TAK Short Communication Effects of Mimosa Bark Usage on Some Properties of Particleboard Gökay NEML‹, Gürsel ÇOLAKO⁄LU Karadeniz Technical University, Faculty of Forestry, Trabzon - TURKEY Received: 05.04.2004 Abstract: The objective of this study was to determine the effect of mimosa bark usage on the formaldehyde emission, physical and mechanical properties of particleboard. Fifteen panels from black locust (Robinia pseudoacacia L.) wood containing mimosa bark in a core layer at different ratios were manufactured. Three boards without bark addition were produced as control boards. Formaldehyde emission, modulus of rupture, modulus of elasticity, internal bond strength and thickness swelling of the specimens were tested. It was found that panels made from black locust wood had the highest mechanical properties while panels containing mimosa bark had the lowest. Bark usage significantly improved (decreased) the formaldehyde emission and thickness swelling of particleboard. Based on the findings of this study, it appears that mimosa bark can be used in the manufacture of particleboard panels. Bark content was found to be a raw material parameter influencing the properties of the panels. Key Words: Particleboard, mimosa bark, formaldehyde emission, mechanical properties, physical properties. Mimosa Kabu¤u Kullan›m›n›n Yongalevhan›n Baz› Özellikleri Üzerine Etkisi Özet: Bu çal›flman›n amac›, mimosa kabu¤u kullan›m›n›n yongalevhan›n fiziksel ve mekanik özellikleri ile formaldehit emisyonu üzerine etkisinin belirlenmesidir. Yalanc› akasya (Robinia pseudoacacia L.) odunu kullan›larak orta tabakas›nda farkl› oranlarda kabuk ihtiva eden 15 adet levha üretilmifltir. Üç levha kabuk kullan›lmadan kontrol amaçl› üretilmifltir. Üretilen levhalar üzerinde; formaldehit emisyonu, e¤ilme direnci, elastiklik modülü, yüzeye dik çekme direnci ve kal›nl›¤›na fliflme oran› deneyleri yap›lm›flt›r. Yalanc› akasya odunundan üretilen .