TAILIEUCHUNG - Modification the characterization of epoxy polyester blend by using titanium dioxide filler

Epoxy resin blended with Unsaturated polyester resin and filled with TiO2 filler. ultrasonic mixing process. TiO2 nanoparticles were used as reinforcement in prepared by cast molding method with filler volume fractions (0%,1%, 2%, and 3% ). | Modification the characterization of epoxy polyester blend by using titanium dioxide filler International Journal of Mechanical Engineering and Technology IJMET Volume 10 Issue 03 March 2019 pp. 1492 1501 Article ID IJMET_10_03_151 Available online at http ijmet JType IJMET amp VType 10 amp IType 3 ISSN Print 0976-6340 and ISSN Online 0976-6359 IAEME Publication Scopus Indexed MODIFICATION THE CHARACTERIZATION OF EPOXY POLYESTER BLEND BY USING TITANIUM DIOXIDE FILLER Abeer adnan abd Polymer Department College of Engineering Materials Babylon University Iraq ABSTRACT Epoxy resin blended with Unsaturated polyester resin and filled with TiO2 filler. ultrasonic mixing process. TiO2 nanoparticles were used as reinforcement in prepared by cast molding method with filler volume fractions 0 1 2 and 3 . The thermal conductivity constant hardness compression strength wear impact strength and DSC were studied. Compression strength wear loss thermal conductivity constant DSC FTIR UV atomic force were studied. The experimental results showed that the thermal conductivity constant decrease hardness increase with filler content increase . Titanium dioxide content in epoxy polyester blend matrix was dispersed and investigated by using ultrasonic technique .Sample four give the maximum value of compression strength. The glass transition temperature melting point and degree of crystallization decrease by adding titanium dioxide. Key words Epoxy unsaturated polyester TiO2 nanofiller Mechanical properties thermal stability polymer blend Cite this Article Abeer Adnan Abd Modification the Characterization of Epoxy Polyester Blend By Using Titanium Dioxide Filler International Journal of Mechanical Engineering and Technology 10 3 2019 pp. 1492 1501. http IJMET JType IJMET amp VType 10 amp IType 3 1. INTRODUCTION One of the ways Nano science has advanced Polymer composites industries of high- performance for automotive and aircraft .

• Hoá học
• Ultrasonic mixing process
• Cast molding method
• Filler volume fractions
• Epoxy unsaturated polyester
• Thermal conductivity constant
• Composite solid electrolyte
• X ray diffraction
• Differential thermal analysis
• Electrical conductivity
• Dielectric constant
• Dielectric loss