TAILIEUCHUNG - Steel fibers pull-out after exposure to high temperatures and its contribution to the residual mechanical behavior of high strength concrete

This paper analyzes the effect of temperature on steel fibers pull-out mechanism from a high strength concrete matrix and its contribution to the residual mechanical behavior of Steel Fiber Reinforced High Strength Concrete (SFRHSC). Pull-out tests of straight and hooked end fibers and uniaxial tension tests on the fiber filaments exposed to room and high temperature (300 C, 375 C and 475 C) were performed. Additionally, two SFRHSC incorporating 30 kg/m3 and 60 kg/m3 of hooked end steel fibers and a plain High Strength Concrete (HSC) exposed to the same temperatures were studied. Uniaxial compression tests and bending tests on notched prisms were used to characterize the composite material. The experimental results were analyzed with the aid of a pull-out model and a meso-model for SFRHSC, both developed by the authors. It is shown that hooked end fibers pull-out strength was reduced after the exposure to high temperatures. Since concrete strength only contributes in a small region surrounding the hooks, the pull-out strength reduction can be mainly attributed to the reduction of steel strength and frictional effects due to high temperature exposition. HSC tension strength reduction begins earlier and it is proportionally greater than pull-out strength reduction. As a consequence, HSC bending strength decreases faster than SFRHSC strength. | Steel fibers pull-out after exposure to high temperatures and its contribution to the residual mechanical behavior of high strength concrete

TAILIEUCHUNG - Chia sẻ tài liệu không giới hạn
Địa chỉ : 444 Hoang Hoa Tham, Hanoi, Viet Nam
Website : tailieuchung.com
Email : tailieuchung20@gmail.com
Tailieuchung.com là thư viện tài liệu trực tuyến, nơi chia sẽ trao đổi hàng triệu tài liệu như luận văn đồ án, sách, giáo trình, đề thi.
Chúng tôi không chịu trách nhiệm liên quan đến các vấn đề bản quyền nội dung tài liệu được thành viên tự nguyện đăng tải lên, nếu phát hiện thấy tài liệu xấu hoặc tài liệu có bản quyền xin hãy email cho chúng tôi.
Đã phát hiện trình chặn quảng cáo AdBlock
Trang web này phụ thuộc vào doanh thu từ số lần hiển thị quảng cáo để tồn tại. Vui lòng tắt trình chặn quảng cáo của bạn hoặc tạm dừng tính năng chặn quảng cáo cho trang web này.